| 1. | Transversely isotropic elasticity of porous alumina film
多孔氧化铝薄膜横观各向同性弹性性质的研究 |
| 2. | It was also found that the light emitted from porous alumina could excite the pl of dbo - ppv
这是由于多孔氧化铝的纳米结构很好地吸附了m ppv分子，并阻止它的聚集。 |
| 3. | Because of the above features , the porous alumina was used as a desirable template to fabricate ordered nanowire arrays
这些特性表明，多孔氧化铝是一种很好的制备有序纳米线阵列的模板材料。 |
| 4. | In this paper porous alumina membrane is used as template to synthesize ni nanoarray and electrical deposition is applied
本文以纳米孔的多孔氧化铝膜作为模板，采用电化学沉积法在孔内合成出高度有序的镍纳米阵列体系。 |
| 5. | Four peaks in the photoluminescence ( pl ) spectra of the composite of porous alumina and dbo - ppv , which were contributed from both of dbo - ppv and porous alumina , were found
多孔氧化铝dbo干pv复合体系的pl谱出现了四个峰，多孔氧化铝的峰位置没有发生改变， dbo ppv的三个峰发生了90urn的蓝移。 |
| 6. | The multiwalled carbon nanotube array was fabricated by chemical vapor deposition ( cvd ) in the template of porous alumina in the presence of a catalyst such as cobalt and the carbonaceous source of c2h2
以多孔氧化铝为模板，金属钴为催化剂，乙炔为碳源，通过化学气相沉积法制备出多壁碳纳米管阵列。 |
| 7. | Nanometer pore arrays alumina films were prepared by anodizing of highly pure aluminum foils in sulfuric and oxalic acid solution . the porous alumina layers were detached from the al substrate by using step - down voltage or solution method
在草酸和硫酸溶液中，通过阳极氧化高纯铝片的方法制备了纳米氧化铝膜孔阵列，用阶梯降压法或溶解法将氧化铝膜层和铝基底分离。 |
| 8. | We have got porous alumina in the aqueous solution of oxalic acid with appropriate concentration through two - step anodic oxidation . the resultant porous alumina membranes have relatively ordered hexagonal pore arrays , which consist of separated nanopores perpendicular to the film surface , parallel to each other and with uniform pore diameter . the pore diameter can be controlled by varieties of immersion time in acid
实验表明，在适当浓度的草酸中，铝电化学氧化形成多孔氧化铝，其表面形貌研究表明，多孔氧化铝膜中孔径均匀，垂直于表面且彼此分立而平行的纳米级微孔，通过扩孔处理可以方便控制孔径大小。 |